News Release from: Schaeffler (UK) | Subject: Coatings for bearings
Edited by the Processingtalk Editorial Team on 06 November 2007

Bearing material / coatings for harsh
environments

Dr Steve Lacey, Engineering Manager at Schaeffler UK, discusses the selection of appropriate special coatings or corrosion-resistant materials for rolling bearings operating in harsh environments

By investing in a brand new development centre for the surface coating of bearing components and by continuing to invest in R+D activities, the Schaeffler Group can offer customers a comprehensive range of special bearing materials and coatings, designed to improve performance and protect their bearings from corrosion, wear, friction and slippage in every application The new coatings development centre, opened earlier this year at the Schaeffler Group headquarters in Herzogenaurach, Germany, will research and develop new processes and combinations of unique materials and bearing coatings technologies

While the standard Schaeffler INA and FAG branded bearings guarantee the customer optimum performance and a long service life, in some harsh operating environments or for special applications, a standard bearing material or coating may need to be upgraded in order to prevent wear or corrosion of the bearing and to improve the service life.

Coatings are applied to the surfaces of rolling bearing components without forming a material bond, for example by diffusion between the coating and base material.

In many cases, it is sufficient to coat only part of the bearing or one of the parts that come into rolling contact.

Schaeffler can advise customers when a coating is appropriate and what type should be used in certain applications.

As well as offering special corrosion-resistant coatings such as Corrotect , Protect A and Protect B, Schaeffler can also provide a range of corrosion-resistant materials for rolling bearings that operate in corrosive environments.

While standard steel bearing materials provide satisfactory corrosion resistance in many applications, for higher performance requirements, highly corrosion-resistant, nitrogen alloyed martensitic HNS (high nitrogen) steels - such as the Schaeffler Cronidur and recently developed Cronitect steels - are also available.

Cronitect is a new high-grade martensitic hardening steel, developed for rolling bearings, which offers maximum corrosion resistance under extreme conditions, for example, in dry running applications or when the bearings are in contact with aggressive media such as water, acids and cleaning agents.

In contrast to Cronidur, Cronitect has nitrogen introduced into the structure by means of a surface layer hardening process.

Based on the consistent refinement of high-grade NIROSteels, Cronitect achieves a very high hardness through its unique chemical composition, in combination with a new thermo-chemical surface layer treatment process.

The material is therefore able to withstand extreme conditions, including salt spray testing in accordance with DIN 50021 SS without any problems, even after 600 hours.

Cronitect's resistance to corrosion is many times better than that of conventional NIROSteels.

Rolling bearings that use Cronitect come in either a sealed or a non-sealed version.

The name Cronitect is derived from the chemical composition of the material and from its special heat treatment process.

The 'tect' suffix is found in other Schaeffler coating products and refers to the excellent corrosion protection of the material.

Both Cronidur and Cronitect are superior to conventional corrosion-resistant steels for rolling bearings in terms of corrosion resistance, wear resistance and fatigue strength.

This means they have very high corrosion resistance against aqueous media and heavily diluted acids, alkalines or salt solutions.

Potential applications can be found in clean rooms, electronic component manufacturing plants, pharmaceuticals and food production.

Other special materials include ceramic rolling bearing components, which provide excellent characteristics for certain applications.

Silicon nitride balls, for example, are light and offer a longer operating life than standard steel ball elements.

High performance plastics such as PEEK can also be used for bearing components operating in corrosive environments.

PEEK is resistant to high temperatures and, depending on the load, is suitable for operating temperatures of up to 250C.

The wear resistance is strongly influenced by the filler materials and is significantly better than that of the standard material PA66 with glass fibre reinforcement that is often used for bearing cages.

Schaeffler offers three special coatings that improve the corrosion-resistance and/or wear resistance of the surface.

Corrotect is a relatively low cost, 0.5 to 5um thick zinc alloy coating with cathodic protection, which is effective against condensation, rainwater, contaminated water and weak alkaline and weak acidic cleaning agents.

Under load, the coating is compacted into the surface roughness profile and is partly worn away.

The chromate coating and the passivation increase anti-corrosion protection and contribute to the optical appearance of the component.

Corrotect is ideal for small bearings and bearing mating parts that need to have a greater resistance to corrosion, for example drawn cup needle roller bearings with open ends and thin-walled components in large numbers.

Protect A is a pure, matt grey coloured chromium coating with a pearly surface structure.

The coating is applied by electroplating, so the coated parts retain full dimensional stability.

Lubricant is retained between the pearls, therefore effective anti-wear protection is achieved, even under mixed friction or slippage conditions.

During running-in, the rolling elements and seals burnish the surface, which leads to reduced friction coefficients.

Protect A is resistant to various chlorides, oils, sulphur compounds, chlorine compounds and weak acidic media.

Ideal for aggressive atmospheres at high temperatures, Protect B is a coating comprising two layers: a thin chromium coating covered by a chromium mixed oxide layer, the latter providing corrosion-resistance by supporting the lubricant.

The coating offers high anti-wear protection together with high anti-corrosion protection.

Protect B is also ideal for applications in which continuous lubrication of the bearing cannot be guaranteed.

For corrosion and fretting corrosion, Schaeffler has developed a range of coatings to protect bearings, including zinc iron coatings for rolling mill applications, zinc nickel for bearings used in automotive engineering and zinc phosphate for applications exposed to salt or sea water.

Black oxidising coatings are also available, which are ideally suited to rollers and rings for bearings in wind turbines and rail traction motor bearings.

These coatings are ideally suited to applications in which there is a minor risk of slippage.

Thin dense chromium coatings (TDC) also offer effective wear protection in mixed-friction conditions for small ball and roller bearings and are suitable for raceways on high precision bearings and spindle bearings.

A copper coating is also available for emergency lubricant on bearing cages, whilst silver coatings are used for the same purpose on aerospace bearings.

Titanium nitride offers the customer wear protection in jet engine bearings.

As many rolling bearings are used in electric motors, the bearings must be electrically insulated to prevent passage of electric current.

The outside diameters and the faces, or alternatively the bore and the faces, are coated with aluminium oxide.

Schaeffler offers two different coating thicknesses: thick insulating coating with a high resistance to prevent current passage even in moist environments; or a thin insulating coating with a low resistance to current passage.

This coating has sturdier edges due to the lower coating thickness.

A thick coating of aluminium oxide is ideally suited for applications involving three-phase motors and traction motors, whilst a thin coating is ideally suited for applications involving traction motor bearings and tapered bearings for axle bones.

Plastic and Stainless Steel Housed Bearing Units.

The Schaeffler corrosion-resistant coatings and materials can be used throughout the company product range.

For applications in the food industry, for example, the range of Schaeffler housed bearing units (flanged, take-up and plummer block designs) can be protected with various coatings.

The housings and insert bearings can be protected using Corrotect and the housings themselves can also be made from a corrosion-resistant (stainless) sheet steel or plastic (glass fibre reinforced PBT).

Plastic housings are highly resistant to moisture, UV radiation, bacterial and fungal attacks, as well as many chemical media.

These bearing units are used predominantly as locating bearings, but are also suitable as non-locating bearings under low loads and speeds. Request a free brochure from Schaeffler (UK) ...

• Schaeffler (UK): contact details and other news
• Email this article to a colleague
• Register for the free Processingtalk email newsletter
• Processingtalk Home Page

Search the Pro-Talk network of sites